CeramAlloy CBX

REPAIR AND PROTECT ALL TYPES OF EQUIPMENT SUBJECT TO VERY AGGRESSIVE ABRASION.

Engineered to repair deeply damaged components.

Loading

METALCLAD CeramAlloy CBX is a three component, 100% solids, polymer composite specifically formulated to provide effective repair and rebuilding characteristics on all types of equipment subject to severe abrasion.

METALCLAD CeramAlloy CBX is a paste when mixed, so it is easily applied. When cured, however, CBX becomes a metal-hard, highly abrasion resistant compound.

METALCLAD CeramAlloy CBX is the best material to use to protect equipment subject to very aggressive abrasive environments.

Elbows, Pipes, Pumps, Chutes, Deflector Plates, Cyclones, Separators, Vibratory Feeders, Transfer Augers, etc.

  • Extraordinary Abrasion Resistance
  • Trowelable
  • Requires No Heat
  • Unlimited Shelf Life
  • 100% Solids
  • Safe & Simple To Use
  • Heat Exchanger
  • Tube Sheets & Water Boxes
  • Pumps
  • Valves & Pipework
  • Housings & Tanks
  • Cooling Towers

Related Images

Working Life and Cure Times

Ambient Temperature Working Life Full Mechanical Chemical Immersion
59°F 15°C 30 min. 48 hrs. 3 days
77°F 25°C 20 min. 24 hrs. 2 days
86°F 30°C 15 min. 16 hrs. 1 day

Chemical Resistance

Acetic acid (0-10%) G Methyl alcohol G
Ammonium hydroxide (0-10%) EX Mineral Oil EX
Aviation fuel EX Nitric acid (0-10%) EX
Butyl alcohol EX Nitric acid (10-20%) G
Calcium chloride EX Phosphoric acid (0-10%) G
Crude oil EX Potassium chloride EX
Diesel fuel EX Propyl alcohol EX
Ethyl alcohol G Sodium chloride EX
Gasoline EX Sodium hydroxide EX
Heptane EX Sulfuric acid (0-10%) EX
Hydrochloric acid (0-10%) EX Sulfuric acid (10-20%) G
Hydrochloric acid (10-20%) G Toluene G
Kerosene EX Xylene EX

EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.

Technical Data

  • 110 in3 / 1790 cc
  • 0.100 lbs per in3 / 2.76 gm per cc
  • 3.78 ft2 / 0.35 m2
  • Indefinite
  • 100%
Mixing ratio Base Activator Aggregate
By Volume 5 2 14
By Weight 7 2 20

Physical Properties

Typical Values Test Method
Compressive strength 16,000 psi 1125 kg/cm2 ASTM D-695
Flexural strength 9,500 psi 665 kg/cm2 ASTM D-790
Hardness - Shore D 86 ASTM D-2240
Tensile Strength 2,500 psi 176 kg/cm2 ASTM D-2370
Tensile Shear Adhesion (CL+AC primer to substrate)
Steel 4000 psi 280 kg/cm2 ASTM D-1002
Aluminum 2500 psi 175 kg/cm2 ASTM D-1002
Copper 3000 psi 210 kg/cm2 ASTM D-1002
Stainless Steel 4100 psi 287 kg/cm2 ASTM D-1002