SpeedAlloy QS

THE SUPER FAST LEAK STOPPER!

Seal leaks in minutes, without heat.

Available in unique, convenient ENECON® ‘A – Packs.’

METALCLAD SpeedAlloy QS begins to harden in just seconds. It is a 100% solids, high performance polymer composite that can be used to make effective repairs to all types of pipes, tanks and equipment which must be returned to service very quickly or where shut downs are not possible.

METALCLAD SpeedAlloy QS is a two-component system. The simple 1:1 mixing ratio insures easy mixing. It cures to super tough composite.

  • Ultra Fast Curing
  • Trowelable
  • Requires No Heat
  • Unlimited Shelf Life
  • 100% Solids
  • Safe & Simple To Use
  • Pipes & Tanks
  • Sumps
  • Radiators & Fuel tanks
  • Cracked & holed casings
  • Seams

Technical Data

  • 10.5 in3 / 172 cc
  • 0.085 lbs per in3 / 2.33 gm per cc
  • 42 in2 / 0.027 m2
  • Indefinite
  • 100%

Related Images

Mixing ratio Base Activator
By Volume 1 1
By Weight 1 1

Working Life and Cure Times

Ambient Temperature Working Life Light Load Full Mechanical
41°F 5°C 5 min. 30 min. 2 hrs.
59°F 15°C 2 min. 10 min. 1 hrs.
77°F 25°C 1 min. 5 min. 40 min.
86°F 30°C 45 sec. 3 min. 30 min.

Physical Properties

Typical Values Test Method
Compressive strength 11,000 psi 770 kg/cm2 ASTM D-695
Hardness - Shore D 80 ASTM D-2240
Tensile Shear Adhesion    
Steel 2100 psi 147 kg/cm2 ASTM D-1002
Aluminum 1900 psi 133 kg/cm2 ASTM D-1002
Copper 1800 psi 126 kg/cm2 ASTM D-1002
Stainless Steel 2000 psi 140 kg/cm2 ASTM D-1002

SpeedAlloy QS has an extremely fast initial set time, making it the ideal material for stopping the flow and effectively plugging active leaks. The use of SpeedAlloy QS, allows time for proper surface preparation and application of either standard SpeedAlloy or DurAlloy (over the SpeedAlloy QS) for a long-term repair.