GENERAL PURPOSE HIGH PERFORMANCE POLYMER COMPOSITE COATING SYSTEM FOR INDUSTRIAL/COMMERCIAL APPLICATIONS IN STANDARD CHEMICAL ENVIRONMENTS
CHEMCLAD GP is a two component, 100% solids, high performance, general purpose polymer system used for creating an outstanding corrosion and chemical resistant protective coating on all types of equipment and structures.
CHEMCLAD GP is simple to use. It mixes easily and can be applied by brush, roller or spray. It is available in different colors to simplify overcoating. This high gloss coating yields a surface that’s not only functional, but also aesthetically pleasing. CHEMCLAD® GP is also available in ‘safety yellow.’
CHEMCLAD GP provides extraordinary protection to machinery equipment and structures in some of the most severe industrial environments.
Prior to applying CHEMCLAD GP to concrete and / or cementitious substrates, the surface should be treated with CHEMCLAD® P4C to seal the surface, minimize outgassing and insure that optimum adhesion is obtained.
Note: Other colors are available on a “special order” basis. However, there are minimum / multiple quantity requirements for such orders and there may be an increase in cost. Additionally, due to formulation restrictions, not all colors are possible for all materials. Speak to your local ENECON Sales Representative for more information.
Due to monitor / printer differences, actual colors may vary slightly from the representations appearing in this chart.
Working Life and Cure Times
|Ambient Temperature||Working Life||Touch Dry||Maximum Overcoating||Full Cure|
|41°F||5°C||110 min.||55 hrs.||96 hrs.||10 days|
|59°F||15°C||90 min.||24 hrs.||48 hrs.||6 days|
|77°F||25°C||70 min.||16 hrs.||24 hrs.||4 days|
|86°F||30°C||55 min.||8 hrs.||16 hrs.||3 days|
|Typical Values||Test Method|
|Tensile Shear Adhesion|
|Steel||3700 psi||253 kg/cm2||ASTM D-1002|
|Aluminum||2700 psi||182 kg/cm2||ASTM D-1002|
|Copper||3000 psi||161 kg/cm2||ASTM D-1002|
|Stainless Steel||3500 psi||232 kg/cm2||ASTM D-1002|
|Elcometer Adhesion - to properly prepared cementitious surfaces is greater than the cohesive strength of the substrate.|
CHEMCLAD P4C Technical Data
Theoretical coverage rate per kg. @ 3 mils   70 - 80 ft2 / 6 - 7 m2
|Ambient Temperature||Working Life||Minimum Overcoating||Maximum Overcoating|
|41°F||5°C||120 min.||16 hrs.||48 hrs.|
|59°F||15°C||75 min.||12 hrs.||36 hrs.|
|77°F||25°C||60 min.||8 hrs.||24 hrs.|
|86°F||30°C||50 min.||5 hrs.||16 hrs.|
|Acetic acid (0-10%)||G||Methyl ethyl ketone||NR|
|Acetic acid (10-20%)||NR||Naptha||EX|
|Acetone||NR||Nitric acid (0-10%)||G|
|Aviation fuel (JP-4)||EX||Nitric acid (10-20%)||G|
|Calcium chloride||EX||Phosphoric acid (0-10%)||G|
|Carbon tetrachloride||G||Phosphoric acid (10-20%)||G|
|Crude oil||EX||Propyl alcohol||EX|
|Ethyl alcohol||G||Sodium chloride||EX|
|Heptane||EX||Sulfuric acid (0-10%)||EX|
|Hydrochloric acid (0-10%)||EX||Sulfuric acid (10-20%)||EX|
|Hydrochloric acid (10-20%)||EX||Toluene||NR|
EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.
NR - Not Recommended